Elastic adhesiveSuper X series
Elastic adhesive | Super X
Cemedine Super X is an innovative one-part, quick cure adhesive with three key features: "Pressure-sensitive adhesion", "Elastic adhesion" and "Solvent-free adhesion", which are the ideal properties of adhesives. It is used around the world.
Super X products allow for adhesion of various types of plastics, rubbers and ceramics over an extensive range, and also over different types of metals. These products provide excellent adhesion over a very extensive range of materials, eliminating the need for selecting a particular adhesive for each type of material, as in the case of conventional adhesives.
Curing reaction is caused by moisture absorbed from the air. Pressure-sensitive range is reached in this curing process about 10 min after application. If adherends are put together during this time, they bind instantaneously as in the case of rubber contact adhesive, eliminating the need for temporary fixation. Easy-to-use, safe, and clean adhesive featuring one-part solventless capable of quick curing at room temperature is provided.
Super X as elastic adhesives does not peel off. Once materials are adhered, Super X provides durability in the range from low temperature (-60°C) to high temperature (120°C). Because of the rubber state of the hard film, the Super X sufficiently follows expansion, shrinkage and other changes of adherends.
There is not including low molecular weight cyclosiloxane. (D3 to D10 Cyclosiloxane compound)
[Method 1: Single-sided application]
[Method 2: Double-sided application (like contact cement)]
|Adherends||Tensile shear adhesive strength
after 7-day curing
|Metal||Steel plate (SPCC, SPCD)||3.32||CF|
|Unplasticized polyvinyl chloride||3.08||CF|
|PET(Polyethylene terephthalate)||2.22||CF3 AF7|
CF:Cohesion Failure, AF:Adhesive Failure, MF:Failure Modes
Coated on both sides, 50µm thick (one side),tension speed between adherends: 50mm/min
*1 and *2: Surface preparation causes adhesive strength to become uneven; it must be confirmed in advance.
*3: Primer (Cemedine PP-7F) to be used.
|Adherends||Peeling adhesive strength
after 7-day curing
|CR (Chloroprene rubber) (*)||0.43||AF|
(*)…Degreasing by MEK after treatment by sandpaper (#120)
|Chemicals||Tensile shear strength
after dipping in chemicals
|Acetic acid (1% water solution)||2.05||CF4 AF6|
|Acetic acid (10% water solution)||1.22||CF3 AF7|
|Sulfuric acid (3% water solution)||2.93||CF2 AF8|
|Sulfuric acid (30% water solution)||2.05||AF|
|Sodium hydroxide (1% water solution)||2.84||CF5 AF5|
|Sodium hydroxide (10% water solution)||3.29||CF2 AF8|
|Machine oil (Idemitsu: Mechanic Oil)||2.96||CF5 AF5|
|Salt (10% water solution)||3.16||CF4 AF6|
CF:Cohesion Failure, AF:Adhesive Failure
Adherends : Stainless steel x Stainless steel
Surface preparation : Degreasing with MEK
Coating quantity : Coated on both sides 50μm thick (per side)
Open time : 2 min
Pressing : 2 pinches
Curing : 23°C50%RH x 7 days
Chemical immersion : 23°C x 7 days
Tension speed : 50 mm/min
Destruction State : Confirmation by seeing
*… Deterioration of solvent is observed, but no problem with short-time contact, for example, in washing.